Stainless Steel : 2535nb/UTP 2535nb Wires :

Stainless Steel 2535nb/UTP 2535nb Wires, 2535nb Wires, SS 2535nb/UTP 2535nb Filler Wires, SS 2535nb/UTP 2535nb Wires, 2535nb SS Welding Wire, UTP 2535nb SS TIG welding wire, Stainless Steel 2535nb Wire Rope, 2535nb SS Flux Cored Wire, 2535nb Stainless Steel Mig Welding Wire, SS 2535nb/UTP 2535nb Wire Supplier & Exporters.

Shanti Metal Corporation is a prominent manufacturer, supplier, and exporter of 2535nb / UTP 2535nb Wires in Mumbai India. Wires are manufactured using high-quality raw materials and advanced technology as per globally accepted quality standards. UTP 2535nb is a basic coated electrode with high carbon content for cast steels. UTP 2535 Nb is suitable for joining and surfacing of heat resistant CrNi-cast steels (centrifugal- and mould cast parts) of the same or of similar nature, such as
1.4848 G–X 40 CrNiSi 25 20
1.4852 G–X 40 NiCrSiNb 35 26
1.4857 G–X 40 NiCrSi 35 26
It is used for operating temperatures up to 1150° C in carburized low-sulphur combustion gas, e. g. reforming ovens in petrochemical plants. It has a tensile strength less than 700 MPa. Whether destined for use in challenging scenarios or in standard applications – our high quality SS 2535nb filler wires are ideally suited for all applications in the industrial sectors like transportation and automotive, maintenance and repair, power generation, chemical, oil and gas, pipeline, and brazing industries.

Specification :
range : 0.8 mm, 0.9 mm, 1.0 mm, 1.2 mm, 1.6 mm, 2.0 mm, 2.5 mm, 3.0 mm, 4.0 mm, 5.0 mm.
Diameter : 0.13 mm.
Finish : bright and shiny with no grease on the surface
Temper : annealed
Packing : 4 kg spools, spool wrapped with shrink film then 4 spools packed in carton box, carton boxes in wooden case

Stainless Steel 2535nb/UTP 2535nb Wires Deposit Analysis(%)
C : 0,4
Si : 1,0
Mn : 1,5
Cr : 25,0
Ni : 35,0
Nb : 1,2
Ti : 10,1
Fe : balance

Stainless Steel 2535nb/UTP 2535nb Wires Mechanical Properties
Yield strength RP0,2 (MPa) : > 480
Tensile strength Rm (MPa) : > 680
Elongation A % : > 8
I.V.oC,J(oF,Ft-LBs.) : -