The maximum temperature for the welding is 1500 degree Fahrenheit, at this temperature this alloy wire electrodes proves itself as the best resisting agent against the corrosion and oxidation occurring due to various atmospheric conditions. This is very different from the chromium-nickel stainless steel, as this type of electrode wire is not subjected to the loss of the corrosion resistance due to the carbide precipitation.
It is having the various deposited chemical components like carbon, chromium, silicon, manganese, phosphorus, sulfur and nickel. The welding process used in this is the shielded manual metal arc welding. This is designed to weld the stainless steel of the similar chemical compositions as well as for the overlay carbon steels. This material is an air-hardening type of material which calls for the pre-heating. This electrode interpasses the temperature of not less than the 400 degree Fahrenheit during the welding process.
E410-16 welding rods / welding wires is having a very good application in the surfacing of the steel mill rolls, also in the furnace and the burner parts and moreover in the turbine parts.
SS E410-16 Welding rod / Welding wire : SS Welding Rods / Welding Wire Exporter | Stainless Steel E410-16 Welding Rod | Stainless Steel E410-16 Welding Wire | SS E410-16 Welding Rod / Wire | Stainless Steel Welding Rods / Welding Wire E410-16 SS Welding Rod Exporter | E410-16 Stainless Steel Welding Rod | Welding Rod / Welding Wire | Stainless Steel E410-16 Welding Wire Supplier | Welding Electrode AWS E410-16 Rod/Wire |